Low temperature production of glass ceramics in the anorthite-diopside system via sintering and crystallization of glass powder compacts
Φόρτωση...
Ημερομηνία
Συγγραφείς
Marques, V. M. F.
Tulyaganov, D. U.
Agathopoulos, S.
Ferreira, J. M. F.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Ceramics International
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
The production of glass ceramics (M) with theoretical anorthite-diopside (An-Di) weight ratios of 60/40, 50/50 and 45/55 via sintering and crystallization of glass powder compacts was investigated at different temperatures between 800 and 950 degrees C. The investigated compositions are located in the cross-section of the ternary fluorapatite-An-Di system close to An-Di binary joint, with constant fluorapatite content of 4.8 wt.%. Two different groups of glass powders, with mean particle size of 2 and 10 mu m, were used. The experimental results showed that sintering is almost complete at 800 degrees C, preceding crystallization, which takes place via surface crystallization mechanism. The properties values of the produced GCs, which are the best for the composition close to An-Di eutectic line, are discussed with respect to the evolution of crystalline phases and the microstructure over increasing firing temperature. Under the technology perspective, the investigated processing route is significantly superior in comparison to the attempts reported in earlier studies. (c) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Περιγραφή
Λέξεις-κλειδιά
sintering, glass, glass ceramics, anorthite-diopside, devitrification
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000256950300003
http://ac.els-cdn.com/S0272884207000429/1-s2.0-S0272884207000429-main.pdf?_tid=e6da5572312216e5eca856b773469752&acdnat=1339492667_3b57ea6bf070b45c551b0a6627cadb6c
http://ac.els-cdn.com/S0272884207000429/1-s2.0-S0272884207000429-main.pdf?_tid=e6da5572312216e5eca856b773469752&acdnat=1339492667_3b57ea6bf070b45c551b0a6627cadb6c
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών