Structural analysis and devitrification of glasses based on the CaO-MgO-SiO2 system with B2O3, Na2O, CaF2 and P2O5 additives
Φόρτωση...
Ημερομηνία
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Journal of Non-Crystalline Solids
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
Glasses, whose basic composition was based on the CaO-MgO-SiO2 system and doped with B2O3, P2O5, Na2O, and CaF2, were prepared by melting at 1400 degrees C for 1 h. Raman and infrared (IR) spectroscopy revealed that the main structural units in the glass network were predominantly Q(1) and Q(2) silicate species. The presence of phosphate and borate units in the structure of the glasses was also evident in these spectra. X-ray analysis showed that the investigated glasses devitrified at 750 degrees C and higher temperatures. The crystalline phases of diopside and wollastonite dominated, but weak peaks, assigned to akermanite and fluorapatite, were also registered in the diffracto-grams. The presence of B2O3, Na2O, and CaF2 had a negligible influence on the assemblage of the crystallized phases, but it caused a reduction of crystallization temperature, comparing to similar glasses of the CaO-MgO-SiO2 system. (c) 2005 Elsevier B.V. All rights reserved.
Περιγραφή
Λέξεις-κλειδιά
crystallization, glass cerarnics., raman scattering, optical spectroscopy, ftir measurement, raman spectroscopy, alkali silicates, boro-silicates, silicates, structure, short-range order, lithium borate glasses, silicate-glasses, vibrational spectroscopy, nucleating-agents, phosphate-glasses, raman, ceramics, spectra, crystallization, crystals
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000236226700004
http://ac.els-cdn.com/S0022309305008161/1-s2.0-S0022309305008161-main.pdf?_tid=894653843976bb6e8f5521b39eb4e559&acdnat=1339492758_3e9e651ffba7455cb072c8d641c1ef50
http://ac.els-cdn.com/S0022309305008161/1-s2.0-S0022309305008161-main.pdf?_tid=894653843976bb6e8f5521b39eb4e559&acdnat=1339492758_3e9e651ffba7455cb072c8d641c1ef50
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών