Synthesis of glass-ceramics in the CaO-MgO-SiO2 system with B2O3, P2O5, Na2O and CaF2 additives
Φόρτωση...
Ημερομηνία
Συγγραφείς
Tulyaganov, D. U.
Agathopoulos, S.
Ventura, J. M.
Karakassides, M. A.
Fabrichnaya, O.
Ferreira, J. M. F.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Journal of the European Ceramic Society
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
Glass-ceramics based on the CaO-MgO-SiO2 system with limited amount of additives (B2O3, P2O5, Na2O and CaF2) were prepared. All the investigated compositions were melted at 1400 degrees C for 1 h and quenched in air or water to obtain transparent bulk or frit glass, respectively. Raman spectroscopy revealed that the main constituents of the glass network are the silicates Q(1) and Q(2) units. Scanning electron microscopy (SEM) analysis confirmed liquid-liquid phase separation and that the glasses are prone to surface crystallization. Glass-ceramics were produced via sintering and crystallization of glass-powder compacts made of milled glass-frit (mean particle size 11-15 mu m). Densification started at 620-625 degrees C and was almost complete at 700 degrees C. Crystallization occurred at temperatures > 700 degrees C. Highly dense and crystalline materials, predominantly composed of diopisde and wollastonite together with small amounts of akermanite and residual glassy phase, were obtained after heat treatment at 750 degrees C and 800 degrees C. The glass-ceramics prepared at 800 degrees C exhibited bending strength of 116-141 MPa, Vickers microhardness of 4.53-4.65 GPa and thermal expansion coefficient (100-500 degrees C) of 9.4-10.8 x 10(-6) K-1. (c) 2005 Elsevier Ltd. All rights reserved.
Περιγραφή
Λέξεις-κλειδιά
sintering, crystallization, microstructure-final, glass, glass-ceramics, silicate-glasses, nucleating-agents, borate glasses, crystallization, alkaline, wastes, kira
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000236649800020
http://ac.els-cdn.com/S0955221905001378/1-s2.0-S0955221905001378-main.pdf?_tid=41835ab2c0112bac683ba4ccead5a3e5&acdnat=1339492565_e5eb0e2d01d758fcbe4d882cb01305da
http://ac.els-cdn.com/S0955221905001378/1-s2.0-S0955221905001378-main.pdf?_tid=41835ab2c0112bac683ba4ccead5a3e5&acdnat=1339492565_e5eb0e2d01d758fcbe4d882cb01305da
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών