Enhanced bonded aircraft repair using nano-modified adhesives
Φόρτωση...
Ημερομηνία
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Materials & Design
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
The scope of the present work is to investigate if the introduction of a small weight fraction of multi wall carbon nanotubes (CNTs) in a polymer adhesive film can: (a) act as an effective corrosion barrier that inhibits access of the electrolyte to the surface of the aluminium substrate thereby preventing or notably delaying destructive localised aluminium corrosion, (b) lead to a hybrid system with galvanically compatible constituents and (c) enhance the adhesion of the film to the alloy substrate. Electrochemical measurements showed that the incorporation of CNTs into the epoxy film does not mediate the galvanic effect between substrate/coating, whilst it introduces limited localised degradation phenomena into the polymer matrix. However, it reduces the uniform corrosion rate of the film. Lap shear testing showed that the adhesion enhancement that stemmed from CNTs doping was significant in the absence of anodising of the substrate. It is proposed that a bi-layer patch, where the intermediate layer will be the neat polymer film and the over-layer will be the CNTs-reinforced film would be beneficial in terms of optimising the anodic protection by the patch and the galvanic compatibility of the alloy substrate/patch system. (C) 2012 Elsevier Ltd. All rights reserved.
Περιγραφή
Λέξεις-κλειδιά
bonded repair, carbon nanotubes, epoxy, composites, galvanic corrosion, carbon nanotube/epoxy composites, environmental degradation, mechanical-properties, localized corrosion, epoxy composites, reinforced epoxy, aluminum-alloys, behavior, coatings, fracture
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000305988100049
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών