Structural, microstructural and magnetic properties of nanocomposite isotropic Sm(Co(bal)Fe(0.1)M(y)Zr(0.04)B(0.04))(7.5) ribbons with M = Ni, Cu and y=0.09 and 0.12
Φόρτωση...
Ημερομηνία
Συγγραφείς
Makridis, S. S.
Panagiotopoulos, I.
Tsiaoussis, I.
Frangis, N.
Pavlidou, E.
Chrisafis, K.
Papathanasiou, G. F.
Efthimiadis, K.
Hadjipanayis, G. C.
Niarchos, D.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Journal of Magnetism and Magnetic Materials
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
In boron-substituted melt-spun Sm(Co,Fe,Cu,Zr)(7.5)-type alloys a nanocomposite microstructure and high coercivities in both as-spun and short-time annealed ribbons can be obtained. In the present study three different compositions, namely Sm(Co(0.73)Fe(0.1)Cu(0.09)Zr(0.04)B(0.04))(7.5), Sm(Co(0.70)Fe(0.1)Cu(0.12)Zr(0.04)B(0.04))(7.5) and Sm(Co(0.70)Fe(0.1)Ni(0.12)Zr(0.04)B(0.04))(7.5) have been examined in order to investigate the influence of composition on the magnetic properties and the microstructure. Melt-spun ribbons have been obtained and annealing has been followed under argon atmosphere for 30-75 min at 600-870 degrees C. For the as-spun ribbons the TbCu(7)-type of structure and fcc-Co as a secondary phase have been identified in the X-ray diffraction patterns. For the annealed ribbons above 700 degrees C the 1:7 phase transforms into 2:17 and 1:5 phases. The TEM studies have shown a homogeneous nanocrystalline microstructure with average grain size of 30-80 nm. Coercivity values of 15-27 kOe have been obtained from hysteresis loops traced in non-saturating fields. The coercivity decreases with temperature, but it is sufficiently large to maintain values higher than 5 kOe at 380 degrees C. (C) 2008 Elsevier B.V. All rights reserved.
Περιγραφή
Λέξεις-κλειδιά
melt spinning, microstructure, rare-earth permanent magnet, coercivity, permanent-magnets, high coercivity, spun, alloys, substitution, fe
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000257205900006
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών