Low-Temperature Synthesis and Characterization of Gallium Nitride Quantum Dots in Ordered Mesoporous Silica
Φόρτωση...
Ημερομηνία
Συγγραφείς
Dimos, K.
Jankovic, L.
Koutselas, I. B.
Karakassides, M. A.
Zboril, R.
Komadel, P.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
American Chemical Society
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Journal of Physical Chemistry C
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
Semiconducting gallium nitride (GaN) quantum dots (QDs) were synthesized at low temperatures (650 degrees C), using ammonia flow without any organogallium precursor compound, assisted and controlled by an ordered mesoporous silica MCM-41 as host matrix. The final materials exhibit an intense blue shift of the band gap energy compared to the three-dimensional (3D) GaN. MCM-41 hosted GaN QD synthesis is also reported from pyrolysis of an organic precursor, tris(dimethylamido)gallium(M), at 365 degrees C under ammonia flow, with the largest band gap blue shift reported for such synthesized GaN of 0.6 eV. The QDs, involving inorganic precursor, exhibit an average X-ray diffraction estimated diameter of 12.6 angstrom and crystallize in the zinc blende lattice with cubic symmetry (beta-GaN), whereas the hexagonal system is thermodynamically preferred. QDs, based on organic precursor, have hexagonal symmetry (alpha-GaN, wurtzite structure) with an average diameter of 20.6 angstrom. Spectroscopic and structural characterization of the QD-MCM composites showed the successful synthesis of well-defined distributions of QDs, exhibiting luminescence at high energies in the UV region and in some cases defect luminescence, depending on the specific synthetic route.
Περιγραφή
Λέξεις-κλειδιά
semiconductor particles, optical-properties, thermal-stability, molecular-sieve, gan powders, mcm-41, adsorption, zns, nanoparticles, microcrystals
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000298978700147
http://pubs.acs.org/doi/pdfplus/10.1021/jp208011y
http://pubs.acs.org/doi/pdfplus/10.1021/jp208011y
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών