Isolation of the new cubic phases RE4FeGa12-xGex (RE = Sm, Tb; x=2.5) from molten gallium: Single-crystal neutron diffraction study of the Ga/Ge distribution
Φόρτωση...
Ημερομηνία
Συγγραφείς
Zhuravleva, M. A.
Wang, X. P.
Schultz, A. J.
Bakas, T.
Kanatzidis, M. G.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Inorg Chem
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
The compounds RE4FeGa12-xGex (RE = Sm, Tb) were discovered in reactions employing molten Ga as a solvent at 850 degreesC. However, the isostructural Y4FeGa12-xGex was prepared from a direct combination reaction. The crystal structure is cubic with space group Im (3) over barm, Z = 2, and a = 8.657(4) Angstrom and 8.5620(9) Angstrom for the Sm and Tb analogues, respectively. Structure refinement based on full-matrix least squares on F-0(2) resulted in R-1 = 1.47% and wR(2) = 4.13% [1 > 2sigma(1)] for RE = Sm and R-1 = 2.29% and wR(2) = 7.12% [1 > 2sigma(l)] for RE = Tb. The compounds crystallize in the U4Re7Si6 structure type, where the RE atoms are located on 8c (1/4, 1/4, 1/4) sites and the Fe atoms on 2a (0, 0, 0) sites. The distribution of Ga and Ge in the structure, investigated with single-crystal neutron diffraction on the Tb analogue, revealed that these atoms are disordered over the 12d (1/4, 0, 1/2) and 12e (x, 0, 0) sites. The amount of Ga/Ge occupying the 12d and 12e sites refined to 89(4)/11 and 70(4)/30%, respectively. Transport property measurements indicate that these compounds are metallic conductors. Magnetic susceptibility measurements and Mossbauer spectroscopy performed on the Tb analogue show a nonmagnetic state for Fe, while the Tb atoms carry a magnetic moment corresponding to a mu(eff) of 9.25 mu(B).
Περιγραφή
Λέξεις-κλειδιά
solid-state chemistry, exploratory synthesis, physical-properties, aluminum silicides, solvent, nd, chalcogenides, quaternary, uranium, growth
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000179184200022
http://pubs.acs.org/doi/pdfplus/10.1021/ic025544b
http://pubs.acs.org/doi/pdfplus/10.1021/ic025544b
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Επιστημών και Τεχνολογιών. Τμήμα Βιολογικών Εφαρμογών και Τεχνολογιών