A study of the stress-transfer characteristics in model composites as a function of material processing, fibre sizing and temperature of the environment
Φόρτωση...
Ημερομηνία
Συγγραφείς
Paipetis, A.
Galiotis, C.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Composites Science and Technology
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
The micromechanics of reinforcement of a model composite consisting of a high-modulus fibre embedded in epoxy resin has been investigated as a function of processing conditions, namely thermal stresses, fibre sizing, and temperature. The residual stresses on single-fibre coupons were monitored for both long- and short-fibre geometries with the technique of remote laser Raman microscopy (ReRaM). The systems studied consisted of sized and unsized fibre/epoxy systems at room temperature as well as a sized system at 60 degrees C. Each composite was subjected to incremental tensile loading rip to full fragmentation, while the stress in the fibre was monitored at each level of applied strain. The three systems exhibited differences in the residual stress field, with the unsized fibre being in compression. The average stress in the fibre increased linearly with applied matrix strain rip to first fracture. After fracture, the stress in the fibre was found to build from the tips of the fibre breaks, reaching a maximum value at the middle of each fragment. Two different interfacial failure modes were identified, depending on the possible initiation of a mixed-mode matrix crack. At room temperature, the maximum interfacial shear str ess for both systems was of the order of 40 MPa with the sized system exhibiting slightly better adhesion. Ar 60 degrees C, the sized system exhibited interfacial shear stress values of the order of 20 MPa. (C) 1997 Elsevier Science Limited.
Περιγραφή
Λέξεις-κλειδιά
raman microscopy, interface, carbon fibre, epoxy resin, sizing, temperature, stress transfer, shear-strength, fiber, matrix
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://A1997XU50000002
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών