Low temperature synthesis of anorthite based glass-ceramics via sintering and crystallization of glass-powder compacts
Φόρτωση...
Ημερομηνία
Συγγραφείς
Marques, V. M. F.
Tulyaganov, D. U.
Agathopoulos, S.
Gataullin, V. K.
Kothiyal, G. P.
Ferreira, J. M. F.
Τίτλος Εφημερίδας
Περιοδικό ISSN
Τίτλος τόμου
Εκδότης
Elsevier
Περίληψη
Τύπος
Είδος δημοσίευσης σε συνέδριο
Είδος περιοδικού
peer reviewed
Είδος εκπαιδευτικού υλικού
Όνομα συνεδρίου
Όνομα περιοδικού
Journal of the European Ceramic Society
Όνομα βιβλίου
Σειρά βιβλίου
Έκδοση βιβλίου
Συμπληρωματικός/δευτερεύων τίτλος
Περιγραφή
Anorthite based glass-ceramics were synthesized. The investigated glass compositions are located close to the anorthite-rich corner of the fluorapatite-anorthite-diopside ternary system. Glass powder compacts with mean particle size of 2 and 10 mu m were prepared. Sintering behaviour, crystallization and the properties of glass-ceramics were investigated between 800 and 950 degrees C. In the case of specimens made from the finer particles, complete densification was achieved at a remarkably low temperature (825 degrees C) and the highest mechanical strength was obtained at 850 degrees C, but density significantly decreased at higher temperatures. The samples prepared from the larger particles exhibited higher values of density, shrinkage and bending strength within a wider temperature range (825-900 degrees C). Anorthite was predominantly crystallized between 850 and 950 degrees C, along with traces of fluorapatite. Diopside was detected only in the MgO richer compositions. (c) 2005 Elsevier Ltd. All rights reserved.
Περιγραφή
Λέξεις-κλειδιά
sintering, crystallization, microstructure-final, glass-ceramics, anorthite, fabrication, behavior, system
Θεματική κατηγορία
Παραπομπή
Σύνδεσμος
<Go to ISI>://000239770600011
http://ac.els-cdn.com/S0955221905007399/1-s2.0-S0955221905007399-main.pdf?_tid=4ff323250cf5a262dd185e7df9b194e1&acdnat=1339492655_78e3cce902ce32b4a42262486d46783c
http://ac.els-cdn.com/S0955221905007399/1-s2.0-S0955221905007399-main.pdf?_tid=4ff323250cf5a262dd185e7df9b194e1&acdnat=1339492655_78e3cce902ce32b4a42262486d46783c
Γλώσσα
en
Εκδίδον τμήμα/τομέας
Όνομα επιβλέποντος
Εξεταστική επιτροπή
Γενική Περιγραφή / Σχόλια
Ίδρυμα και Σχολή/Τμήμα του υποβάλλοντος
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών